Overview
| Exemplar Number: | hr-001 |
| Figura: | circularis |
| Materia: | non ferro magnetico |
| Product nomen: | Nulla magnetica crossover |
| Typus: | Non ferro magnetico |
| Magnitudo: | 3 1/2″, 4 1/8″, 4 3/4", 5″, 6 1/2″, 6 3/4″, 7″ , 8″ 9″ etc. |
| Latin: | API Spec 7-1 |
| Puritas: | C Si Mn PS Cr Ni Mo Cu N |
| Aspectus: | Circum columna |
| Praecipuum Market: | Mn Cr Ni |
Specification
| item | valorem |
| Locus originis | Sina JiangSu |
| Exemplar Number | |
| Product nomen | Nulla magnetica crossover |
| Type | Non ferro magnetico |
| Magnitudo | 3 1/2″, 4 1/8″, 4 3/4", 5″, 6 1/2″, 6 3/4″, 7″ , 8″ 9″ etc. |
| Standard | API Spec 7-1 |
| Puritas | C Si Mn PS Cr Ni Mo Cu N |
| Aspectus | Circum columna |
| Principalis Market | Mn Cr Ni |
Turba Profile
ZHENJIANG HERUI NEGOTIUM BRIDGE IMP&EXP Co., Ltd.A novum socium pro magna celeritate ferrum et Non magneticum chalybem Agile, porttitor et qualitas ordinantur societas tendentium ad diuturnum tempus societate in Danyang, provincia Jiangsu, area dynamica pro speciali steelRelying in retis socii idonei omnes speciales in speciali chalybe Offerentes breve tempus plumbi servitii Duo socios validam in campo speciali ferro plus quam 25 annos experientiae habent. Main Prodcuts:1/ Altus celeritas ferri gradus : M2 , M35, W4 , W9 bar 2- Tractus 16mm Ground bar 5-15mm depilatum vel rotundum bar 15-150mm.2/ Gradus ferri non magneticus : Occurrunt P550 P530 standardSteelNon magnetici torquem (vel flex ), Crossover Inch size 3 1/2″, 4 1/8″ , 4 3/4, 5″, 6 1/2, 6 3/4″, 7″, 8″ 9″ etc.
FAQ
1. qui sumus?
Fundamur in Jiangsu, Sinis, incipimus ab 2019, in Europam australem vendimus (17.00%), Europam septentrionalem (17.00%), Europa occidentalis (17.00%), Asia orientalis (17.00%), Europa orientalis (17.00%), Meridionalis Asiae (1500%).Sunt circiter 11-50 homines in officio nostro.quomodo praestamus qualitatem?
Vestibulum semper ante massa, eget consequat massa semper a.
Semper finalis metus ante amet;
3. Quid emisti a nobis?
Non Magncetic Chalybe, Proclive Ferro, Die Ferro, Oleum EXERCITATIO Tools, Hardware Tools
4. Cur a nobis non ab aliis praebitoribus emeris?
Novum socium pro High celeritate chalybe et Non magneticum chalybem Agile, eget porttitor et qualitas societatis ordinantur ad longum tempus societate Located in Danyang, provincia Jiangsu, area dynamica pro specialibus steelRelying in retis sociis idoneis
5. Quibus officiis providere possumus?
Accepit Delivery Termini: FOB；
Acceptae Payment Currency: USD, EUR;
Acceptae Payment Type: T/T, L/C, D/PD/A, Promeritum Pecto, PayPal;
Lingua Latina, Sinica, Hispanica, Iaponica, Lusitana, Germanica, Arabica, Gallica, Russica, Coreanica, Italica
HRNM-2 (P530 class) technica vexillum
1. Chemical compositione
Compositio chemica ferri P530 non-magnetici exercetur secundum compositionem chemica fabrica et requisitis in tabula sequenti occurrit:
| Brand | C | Si | Mn | P | S | Cr | Ni | Mo | Cu | N |
| HRNM-2 | ≤0.08 | ≤1.00
| 16.00~19.00 | ≤0.030 | ≤0.020 | 15.00~17.00 | 0.80~1.50 | 0.40~ 0.60 | ≤0.30 | ≥0.40 |
1.Mechanical possessiones
Proprietates mechanicae productorum non magneticarum in statu traditionis occurrentibus requisitis in tabula sequenti:
| Nominal diameter/mm | Cedat imperium.MPa. | Distrahentes fortitudo.MPa. | Prolongatio % | industria impulsum Charpy J | Brinell duritia HB |
| ≤177 | ≥758 | ≥827 | ≥18 | ≥75 | ≥285~ 360 |
| 177-280 | ≥689 | ≥758 | ≥18 | ≥75 | ≥285~ 360 |
Dicta: (1) loco sampling.
Tensile et ictum: specimen longitudinaliter incisum, et centrum specimen 25mm ab externa superficie tubi vel in centro parietis crassitudine.
Duritia: test in sectione transversali intra 20-25mm superficiei corporis tali.
(2) Ictum specimen est v informibus 2mm incisura ad locus temperatus.
3. Magnetic
Relativa permeabilitas μr <1.005 (actu intra 1.003) inductio magnetica intensio gradientis ≤0.04μT
4. Erugo intergranulare
Producta non magnetica ab ASTMA262 methodo E probata sunt, et nulla rima corrosio intergranulare fuit.
5. Nondestructive probatio
Probatio ultrasonica: 100% probatio secundum vexillum ASTME114, criteria acceptatio secundum API 7-1.
6. Metallographic structure
— Frumenti magnitudine major 5;
- Inclusiones non-metallicae: Classis A, CLASS B, Classis C et Classis D inclusiones non-metallicae non sunt maiores quam gradus 1.0 in crasso et subtili serie.
7. Superficies qualitas materiae lucis autocineti: superficies clara esse debet, sine rimas visibilibus, cicatricibus, ovilibus et inclusionibus.
8. Ferro tolerantiae dimensivarum: ad vexillum SY/T5144-2013 referendum, vel ad tolerantiam emptoris requisita.
9. Lassitudine vires
-100k RPM (saltem) +/ -80ksi;
-10k (saltem) +/ -60Ksi;
10. Maximum magnificatio TEXTUS
- Nullae defectus visibiles visibiles erunt, ut DECREMENTUM foramina, bullae, rimas, inclusiones, decorticationes, strationes et maculae albae in cruce sectione-acidi leaching low-potentiam texti test pieces de ferro;
- Acidum leaching potentia TEXTUS humilis campester: communis laxa, laxa centrum, regula segregationis, dot segregationis non sunt maiores quam 1.5 gradus.
Usus et conservatio serrae
◎ In carbide mucro serrae acutissima est, itaque processus usurae ne extremum carbidam esse debet.
◎ apparatus periodicaI purgatio et sustentatio, tolerantiae fusi cursus minor quam h7.
◎ Langiones inter se parallelae esse debent eiusdem diametri 1/3 diametri serrae (formuIti-ripae serrae laminae 1/2).
Cum instaIIion the sawbIade, shaII erit 5-6 dentium altior quam tabula superficiei.
◎ Ante operationem, preme serrae firmitatem, cave nullus ante machinam.Operandi reprehendo utrum machina operaiton bonum sit, noli pascere.Munus periodicum machinae perscriptio, certicaI saltus minor est quam ±0.02MM, et LACINA minor est quam ±0.01.
◎ Post continuum usum, detrahendum et purgandum serram, resinam et scobem ex utraque parte tollendam. Alioquin valeret effectum serrae utendi.
◎ Depositum serrae, ferrum serrare non debet, in involucro originario intus ponitur.
Renovatio sawbIade
◎ Renovatae carbidae serrae, dum iam non acuunt et ad horizontem grossum.Vis utendi sawblade apparatus manifesto crescite.Cum processus materiaI, materiaI visus erupit.Carbida auricula plus quam 0.02MM exhauriunt.
Ad scapulas renovandas, a formali societate molere debet, ut sit certa qualitas laminae post renovationem.