| Gradus No. | Chemical compositione % | |||||||||
| C | P | S | Mn | Si | Cr | Ni | Al | Fe | alii | |
| Maximilianus.(≤) | ||||||||||
| Cr20Ni80 | 0.08 | 0.02 | 0.014 | 0.6 | 0.75-1.60 | 20.0-23.0 | Requiem | ≤0.50 | ≤1.0 | - |
| Cr30Ni70 | 0.08 | 0.02 | 0.014 | 0.6 | 0.75-1.60 | 28.0-31.0 | Requiem | ≤0.50 | ≤1.0 | - |
| Cr15Ni60 | 0.08 | 0.02 | 0.014 | 0.6 | 0.75-1.60 | 15.0-17.0 | 55.0-61.0 | ≤0.50 | Requiem | - |
| Cr20Ni35 | 0.08 | 0.02 | 0.014 | 1 | 1.00-3.00 | 18.0-21.0 | 34.5-36.0 | - | Requiem | - |
| Cr20Ni30 | 0.08 | 0.02 | 0.014 | 1 | 1.00-2.00 | 18.0-21.0 | 30.0-31.5 | - | Requiem | - |
Usus et conservatio serrae
◎ In carbide mucro serrae acutissima est, itaque processus usurae ne extremum carbidam esse debet.
◎ apparatus periodicaI purgatio et sustentatio, tolerantiae fusi cursus minor quam h7.
◎ Langiones inter se parallelae esse debent ejusdem diametri 1/3 diametri serrae (formuIti-ripae serrae laminae 1/2).
Cum instaIIion the sawbIade, shaII erit 5-6 dentium altior quam tabula superficiei.
◎ Ante operationem, preme serrae firmitatem, cave nullus ante machinam.Operandi reprehendo utrum machina operaiton bonum sit, noli pascere.Munus periodicum machinae perscriptio, certicaI saltus minor est quam ±0.02MM, et LACINA minor est quam ±0.01.
◎ Post continuum usum, detrahendum et purgandum serram, resinam et scobem ex utraque parte evellendam.
◎ Depositum serrae, ferrum serrare non debet, in involucro originario intus ponitur.
Renovatio sawbIade
◎ Renovatae carbidae serrae, dum iam non acuunt et ad horizontem grossum.Vis utendi sawblade apparatus manifesto crescite.Cum processus materiaI, materiaI visus erupit.Auriculae auriculae plus quam 0.02MM exhauriunt.
Ad scapulas renovandas, a formali societate molere debet, ut sit certa qualitas laminae post renovationem.