Manufacturer of Anti Magnetic Stainless - Inconel X-750 – Herui Detail:
Description
Inconel X-750 (UNS N07750 / W. Nr. 2.4669 / GH4145 / NiCr15Fe7TiAl) is a precipitation-hardenable nickel-chromium alloy used for its corrosion and oxidation resistance and high strength at temperatures to 1300°F. Although much of the effect of precipitation hardening is lost with increasing temperature over 1300°F, heat-treated material has useful strength up to 1800°F. This kind of alloy also has excellent properties down to cryogenic temperatures.
Typical chemical composition
| Nickel (plus Cobalt) | 70.00 min. |
| Chromium | 14.0-17.0 |
| Iron | 5.0-9.0 |
| Titanium | 2.25-2.75 |
| Aluminum | 0.40-1.00 |
| Niobium (plus Tantalum) | 0.70-1.20 |
| Manganese | 1.00 max. |
| Silicon | 0.50 max. |
| Sulfur | 0.01 max. |
| Copper | 0.50 max. |
| Carbon | 0.08 max. |
| Cobalt | 1.00 max |
Application
Oil and gas production
Gas turbine engines
Nuclear engineering
Equal grade
GH4145, UNS N07750, Alloy X-750, W. Nr. 2.4669
Forms available
Plate, sheet, strip, wire, rod, bar, forging
Product detail pictures:
Related Product Guide:
We have many excellent staff members good at marketing, QC, and dealing with kinds of troublesome problem in the production process for Manufacturer of Anti Magnetic Stainless - Inconel X-750 – Herui, The product will supply to all over the world, such as: Bangkok, Georgia, Guinea, we always keep our credit and mutual benefit to our client, insist our high quality service to moving our clients. always welcome the our friends and clients to come and visit our company and guid our business, if you are interested in our products, you can also submit your purchase information online, and we will contact you immediately, we keep our highly sincere cooperation and wish everything in your side are all well.
The use and maintain of the sawblade
◎ The carbide tip of sawblade is very sharp, so process of using must be prevent the carbide tip.
◎ PeriodicaI cleaning and support the machine,the spindle’s running tolerance must be less than h7.
◎ The flanges must be parallel to each other,must be of the same diameter 1/3 of the sawblade’s diameter(formuIti—rip saw blade is 1/2.
◎ When instaIIion the sawbIade,it shaII be 5-6 teeth higher than board surface．
◎ Before operation,check the firmly of the sawblade,be sure nobody in front of the machine. Do not feed of operation check whether the machine is good for operaiton. Periodical check the function of the machine,the certicaI jump is less than ±0.02MM,and the flap is less than ±0.01.
◎ After continuous use,must be removed and cleaning the sawblade,get rid of the resin and sawdust of the sawblade of both sides.Other wise it would beinfluence the effect of using the sawblade.
◎ Deposit of the sawblade,must not be layer the sawblade,it is putted in the originaI package inside.
The renovate of the sawbIade
◎ The renovate of the carbide sawblade While it no longer sharpen and the horizontaI piece coarseaess. The power of using sawblade machine obviously Increase. When process materiaI,the materiaI appearred burst. The carbide tip exhaust more than 0.02MM.
◎ For the renovate the sawblade,it shouId be grinding by the a formal company, so be sure the quality of the sawblade after renovating.
By Lulu from Saudi Arabia - 2017.01.11 17:15
This company can be well to meet our needs on product quantity and delivery time, so we always choose them when we have procurement requirements.
By Genevieve from Chile - 2018.02.08 16:45